CLINICAL ORTHOPAEDICS AND RELATED RESEARCH, cilt.470, sa.7, ss.1826-1833, 2012 (SCI-Expanded)
Gas sterilization (eg, ethylene oxide [EtO] and gas plasma) was introduced for polyethylene to reduce oxidation due to free radicals occurring during radiation sterilization. Recently, oxidation has been observed in polyethylenes with undetectable levels of free radicals, which were expected to be oxidatively stable. It is unclear whether in vivo oxidation will occur in unirradiated inserts sterilized with EtO. We collected 20 EtO-sterilized tibial inserts at revision surgeries. We assessed oxidative using Fourier transform infrared spectroscopy and mechanical properties using the small punch test. Surface damage was assessed using damage scoring techniques and micro-CT. Oxidation indexes were low and uniform between the regions. The subtle changes did not affect the mechanical properties of the polymer. The dominant surface damage modes included burnishing, abrasion, and third-body wear. There was no evidence of delamination in the retrievals. The retrieved EtO-sterilized UHMWPE retrievals remained stable with respect to both oxidative and mechanical properties for up to 10 years in vivo. We did observe slight measurable amounts of oxidation in the inserts; however, it was far below levels that would be expected to compromise the strength of the polymer. Due to the stable oxidative and mechanical properties, EtO-sterilized tibial components appear to be an effective alternative to gamma-sterilized inserts, at least in short-term implantations.